5W diode laser and Cricut brand infusible ink. I don’t know how deep it penetrates, but 2% @ 45mm/s puts down a muted but easily readable legend on PBT that doesn’t come off with 91% IPA or 100% acetone nail polish remover.
I consider myself a connoisseur of strange engineering projects, but I have to admit, I am kinda lost as to what is going on here.
Are you just etching plastic and rubbing in ink? Do you cover the plastic in ink, etch it and then wipe off excess?
(I mean this as a serious compliment: You keyboard junkies come up with some really weird shit sometimes. Strange and weird is good!)
I imagine it’s order is:
Ink
Engrave
Wipe off excess ink.
So basically you use a little bit of ink roughly where the typeface will be, when the laser melts the plastic, some pigment will diffuse into the melted plastic, but the unmelted/undiffused stuff is still removable.
If I had to guess this is how it’s actually done on the nicer older keycaps.
Though I could be entirely wrong here…
You’re right. The main challenge was just zeroing in on the point where the plastic softens to let the heated ink penetrate without deforming or burning the keycap. I think there’s potential here to do it better than I have, but I do think I landed on one of 2 or 3 different possible settings that will work decently well.
It’s a low-rent form of dye-sublimation, and I don’t know if they’re using lasers, but dye-sub is one of the preferred ways to add legends to PBT keycaps.
So this is a variation on dye sublimation, one of the main ways legends are printed onto single-color keycaps. The process is basically your second idea and exactly as @Uranium_Green says.
- Coat the area in ink from a marker meant for permanently decorating cloth or various polyesterish plastics. The intended heat source is a glorified clothes iron made for DIY crafting.
- Feed the Laser a simple bitmap image and run it low and slow, so it heats up the plastic but doesn’t melt or char it like on several of the earlier trials in that photo.
This should cause the heat-activated ink to integrate more or less permanently to the polyester-based PBT plastic. Then I clean off the unlasered ink with isopropyl alcohol and/or acetone. The zapped ink doesn’t fade at all, though as you can see it’s not super vibrant.
The sweet spot to do this without charring or melting the keycap is pretty small, though though there’s probably another configuration where you use higher power and quicker movement. There might also be one at even lower power and longer time. I’d seen several people try it, but with weird projects on cheap lasers you’ve typically got to find your own settings. Also, don’t laser ABS; very bad idea.
Awesome, thank you! I could have Googled this, but it is always awesome to get information from someone who can give a better summary.
Since you are closer to the laser etching/cutting aspects than I am (I have a traditional hobby CNC machine and do a ton of 3D printing), I am curious if hight mapping has been integrated into laser etching yet. The reason I ask, is that when I cut fine pitch PCBs, I need to be at very specific depths of cut, usually within 0.1mm or so when precision is required.
Working with small curved surfaces could be problematic for maintaining the correct laser focal point? Maybe? Possibly? Even applying a generic hightmap could allow for better etching consistency IF high precision is required. If that doesn’t matter, cool.
In the low-end space where I play, and I think well into the mid-range, the engraver/cutter is on a 2d gantry, basically a Core-XY 3D printer with no Z axis. I focus manually with thumbscrews and a shim. 3-axis and even 5-axis lasers exist, but I think most of them are industrial class.